Green Synthesis of Graphite Oxide as Metal free Catalyst for Petrochemicals Production

  • Aya Mostafa Mtloob
  • D. Guirguis
Keywords: Graphite, Graphite Oxide, Graphene, Ethanol Redox Reaction .

Abstract

Graphite oxide was synthesized by the modified Hummer’s method. The degree of the oxidation of the graphite was systematically controlled via the oxidation time, KMnO4 : Graphite wt. ratio and the addition of the phosphoric acid to the oxidation media. The Physicochemical properties of the synthesized graphite oxide are investigated by using different techniques ; XRD,  FTIR, zeta potential, and TEM. It was found that the structure of the expanded graphite can be easily and remarkably disordered by oxidation. Three phases of interlayer distances were identified at 3.4 , 4 and 6A⁰ , specified for the pristine graphite, intermediate and the fully expanded graphite oxide respectively  These phases were cooresponding to the compositions : epoxide, carboxyl and hydroxyl groups respectively . as confirmed by FTIR.

The catalytic activity of the prepared graphite oxide samples was tested for petrochemical production from the ethanol conversion reaction at different reaction temperature 100-250oC and resulted pressure ranging  40-92 atm . The converted products were mainly composed of  acetone, ethylene, acetaldehyde, diethylether, and heavyhydrocarbons( >c). Acetone was found to be the main product at all reaction temperatures with selectivity ‘‘53-94%’’. XRD and TEM analyses of the prepared samples confirmed  the transformation of  the prepared graphite oxide into graphene like material at reaction temperature 250oC.

Downloads

Download data is not yet available.

References

S. Saxena, T. A. Tyson: ACS Nano 4(2010) 3515-3521.

R. W. Coughlin: Ind. Eng. Chem., 59 (1967), 45

H.S. Song, M.G. Park, W. Ahn: Chem. Eng. J. 253 (2014) 264.

G.Z. Kyzas, D.N. Bikiaris, E.A. Deliyanni: Mater. Lett. 128 (2014) 46.

H.L. Wang, B.A. Kakade, T. Tamaki: J. Power Sources 260 (2014) 338.

B.C. Brodie, Phil. Trans. R. Soc. London Ser. 149 (1859) 249.

Dimiev A., Kosynkin D.V., Alemany L.B., Chaguine P., Tour J.M.: J. Am. Chem. Soc., 134 (2012) 2815.

Hummers’ws,Offeman RE: J.AM chem soc 80(1958), 1339.

Carbon 50 (2012) 3497-3492.

Gudarzi, M. M., Moghadam, M. H. M. & Sharif, F:carbon 64 (2013) 403.

Szabo T, Berkesi O, Forgo P, Josepovits K, Sanakis Y, Petridis D and Dekany I: Chem. Mater.18( 2006) 2740.

H. K Jeong, M H Jin, K P So, S C Lim and Y H Lee: J. Phys. D: Appl. Phys. 42 (2009) 1.

H.K. Jeong, L. Colakerol, M.H. Jin, P.A. Glans, K.E. Smith and Y.H. Lee: Chem. Phys. Lett. 460 (2008) 499.

Y.H. Zu, J.Y. Tang, W.C. Zhu, M. Zhang, G. Liu, Y. Liu, W.X. Zhang, M.J. Jia: Technol. 102 (2011) 8939.

H.K. Jeong, M.H. Jin, K.P. So, S.C. Lim and Y.H. Lee: J. Phys. D: Appl. Phys. 42 (2009) 065418 .

H. Chiang, A. Bhan: J. Catalysis 271 (2010) 251.

Tullo, A.H. Braskem’s Push.: Chem. Eng. News, 89 (2011), 24.

Z. Li, Zhang W, Luo Y, Yang J, Hou JG. : J Am Chem Soc 2009;131(18):6320.

Becerril H A, Mao J, Liu Z, Stoltenberg R M, Bao Z and Chen Y : ACS Nano 2 (2008)463.

Wang X, Zhi L and Mullen K: Nano Lett 8 (2008), 323 .

Du bin S, Gilje S, Wang K, Tung V C, ChaK, HallA S, etal. A one-step, solvothermal reduction method for producing reduced graphene oxide dispersions in organic solvents. ACS Nano 2010;4:3845–52.

Zhu C Z, Guo S J, Fang Y X, Dong S J. Reducing sugar: new-functional molecules for the green synthesis of graphene nanosheets. ACS Nano 2010;4:2429–37.

Published
2016-01-20
How to Cite
Mtloob, A., & Guirguis, D. (2016). Green Synthesis of Graphite Oxide as Metal free Catalyst for Petrochemicals Production. Journal of Progressive Research in Chemistry, 3(2), 131-142. Retrieved from http://scitecresearch.com/journals/index.php/jprc/article/view/559
Section
Articles